EPOMAX LIQUID GLASS (A + B) 3KG Transparent epoxy resin of two components, without solvents

EPOMAX-LIQUID GLASS is a transparent, two-component, liquid-soluble epoxy resin (liquid glass) for creating decorative surfaces.

• It has high mechanical and chemical resistance, excellent adhesion to many types of substrates and very good workability.
• Ideal for indoor applications and generally where the presence of solvents is not desirable.
• Certified with the CE marking as a floor covering product according to the standard EN 13813.

• Chemical base: 2-component epoxy resin
• Shade: transparent
• Viscosity: 450-550 mPa.s (+ 23 ° C)
• Density: 1.10 kg / l
• Mixing ratio (A: B): 100: 58 by weight
• Shelf life: 35-40 min (+ 23 ° C)
• Minimum curing temperature: + 8 ° C
• Initial maturation time: 8 hours (+ 23 ° C)
• Light walkability: 24 hours (+ 23 ° C)
• Final strength: 7 days (+ 23 ° C)
• Maximum application thickness per layer: 5-6 mm
• Indicative intermediate time for each subsequent layer: 1-2 hours (+ 23 ° C)
• Tensile strength: 42 N / mm2
• Elongation at break: 14%
• Shore D Hardness: 75
• Abrasion resistance: AR 0.5 (BCA method, EN 13892-4)
• Impact resistance: IR4 (EN ISO 6272)
• Compressive strength:> 60 N / mm2 (EN 13892-2)
• Flexural strength:> 50 N / mm2 (EN 13892-2)
• Adhesion resistance:> 3 N / mm2 (EN 1542) (concrete break)
• Consumption: depending on the use, the application can be done with a roller, spatula or cast

• Components A (resin) and B (hardener) are packaged in containers with a predetermined mixing ratio.
• Component B is added completely into component A.
• The two components are mixed for about 2 minutes with a low-speed drill (300 rpm).
• It is important to stir both the walls and the bottom of the container so that the hardener is evenly distributed.